Johansson, A., Tsai, H.-C., Aumanen, J., Koivistoinen, J., Myllyperkiö, P., Hung, Y.-Z., Chuang, M.-C., Chen, C.-H., Woon, W. Y., & Pettersson, M. (2017). Chemical composition of two-photon oxidized graphene. Carbon, 115, 77-82. https://doi.org/10.1016/j.carbon.2016.12.091
Published in
CarbonDate
2017Copyright
© 2017 Elsevier Ltd. This is a final draft version of an article whose final and definitive form has been published by Elsevier. Published in this repository with the kind permission of the publisher.
Chemical composition of two-photon oxidized single-layer graphene is studied by micrometer X-ray photoelectron spectroscopy (XPS). Oxidized areas with a size of 2 × 2 μm2 are patterned on graphene by tightly focused femtosecond pulsed irradiation under air atmosphere. The degree of oxidation is controlled by varying the irradiation time. The samples are characterized by four wave mixing (FWM) imaging and Raman spectroscopy/imaging. Micrometer-XPS is used to study local chemical composition of oxidized areas. XPS imaging shows good contrast between oxidized and non-oxidized areas. Gradual oxidation is observed from growth of signals attributed mainly to hydroxyl (Csingle bondOH) and epoxide (Csingle bondOsingle bondC) groups with a minor contribution of carboxylic groups. The highly oxidized areas are characterized by ∼40% of carbon atoms involved in hydroxyl and ∼25% in epoxide groups. The Raman peaks of oxidized graphene are relatively narrow indicating less disordered material than
...
Publisher
PergamonISSN Search the Publication Forum
0008-6223Keywords
Publication in research information system
https://converis.jyu.fi/converis/portal/detail/Publication/26433637